ISO 4802-2:2023

International Standard   Current Edition · Approved on 04 December 2023

Glassware — Hydrolytic resistance of the interior surfaces of glass containers — Part 2: Determination by flame spectrometry and classification

ISO 4802-2:2023 Files

English 15 Pages
Current Edition
47.04 OMR

ISO 4802-2:2023 Scope

This document specifies:

a)       a method for determining the hydrolytic resistance of the interior surfaces of glass containers when subjected to attack by water at (121 ± 1) °C for (60 ± 1) min. The resistance is measured by determining the amount of sodium and other alkali metal or alkaline earth oxides in the extraction solution using flame atomic emission or absorption spectrometry (flame spectrometry);

b)       a classification of glass containers according to the hydrolytic resistance of the interior surfaces determined by the methods specified in this document.

The test method specified in this document might not be applicable to containers whose surfaces have been treated for functional modifications, e.g. silicone (e.g. containers that are ready for direct filling).

Best Sellers

GSO 150-2:2013
 
Gulf Standard
Expiration dates for food products - Part 2 : Voluntary expiration dates
OS GSO 150-2:2013
GSO 150-2:2013 
Omani Standard
Expiration dates for food products - Part 2 : Voluntary expiration dates
OS GSO 2055-1:2015
GSO 2055-1:2015 
Omani Standard
HALAL FOOD - Part 1 : General Requirements
GSO 2055-1:2015
 
Gulf Technical Regulation
HALAL FOOD - Part 1 : General Requirements

Recently Published

ISO 20589:2025
 
International Standard
Glass in building — Determination of the emissivity
ISO 11265:2025
 
International Standard
Environmental solid matrices — Determination of the specific electrical conductivity
ISO 11465:2025
 
International Standard
Sludge and solid environmental matrices — Determination of dry residue or water content and calculation of the dry matter fraction on a mass basis
ISO 9350:2025
 
International Standard
Corrosion of metals and alloys — Testing method of corrosion resistance for hafnium at high temperature and pressure